PPR Tiyo (Random Copolymer Polypropylène) se yon twazyèm -jenerasyon materyèl espesyalize pou tiyo polypropylène, ke yo rele tou Polypropylène Tip 3. PPR plastik tiyo simonte dezavantaj yo nan omopolymer polypropylène, ki ofri ekselan rezistans enpak pandan w ap kenbe estabilite tèmik alontèm -. Plastik PPR tiyo dlo tou asire yon lavi sèvis pi long anba menm tanperati a ak kondisyon presyon entèn yo.
|
Konfòmite estanda: GB/T18742.2-2002 |
||||
|
Seri tiyo |
S5 (1.25MPa) |
S4 (1.6MPa) |
S3.2 (2.0MPa) |
S2.5 (2.5MPa) |
|
Dyamèt deyò nominal (mm) |
Epesè miray (mm) |
Epesè miray (mm) |
Epesè miray (mm) |
Epesè miray (mm) |
|
12 |
2.0 |
|||
|
16 |
2.0 |
2.2 |
2.7 |
|
|
20 |
2.0 |
2.3 |
2.8 |
3.4 |
|
25 |
2.3 |
2.8 |
3.5 |
4.2 |
|
32 |
2.9 |
3.6 |
4.4 |
5.4 |
|
40 |
3.7 |
4.5 |
5.5 |
6.7 |
|
50 |
4.6 |
5.6 |
6.9 |
8.3 |
|
63 |
5.8 |
7.1 |
8.6 |
10.5 |
|
75 |
6.8 |
8.4 |
10.3 |
12.5 |
|
90 |
8.2 |
10.1 |
12.3 |
15.0 |
|
110 |
10.0 |
12.3 |
15.1 |
18.3 |
|
125 |
11.4 |
14.0 |
17.1 |
20.8 |
|
140 |
12.7 |
15.7 |
19.2 |
23.3 |
|
160 |
14.6 |
17.9 |
21.9 |
26.6 |
Fèy done teknik PPR tiyo
|
Atik |
Egzijans |
Kondisyon tès yo |
||
|
Paramèt |
Valè |
|||
|
Sann kontni |
Mwens pase oswa egal a 1.5% |
Tanperati tès la |
600 degre |
|
|
Tanperati k ap fonn |
-PP cristalline-H |
Tpm1 Pi gran oswa egal a 145 degre Tpm2 Pi gran pase oswa egal a 160 degre |
Koule Azòt 50ml / min, to chofaj / refwadisman 10 degre / min, 2 sik |
|
|
PP-B |
Pi gran pase oswa egal a 160 degre |
|||
|
PP-R |
Mwens pase oswa egal a 148 degre |
|||
|
-PP cristalline-RCT |
Tpm1 Mwens pase oswa egal a 143 degre Tpm2 Mwens pase oswa egal a 157 degre |
|||
|
Tan endiksyon oksidasyon |
Pi gwo pase oswa egal a 20min |
Tanperati tès la |
210 degre |
|
|
OIT apre tès idrostatik 95 degre / 1000h |
Pi gran pase oswa egal a 16min |
|||
|
Dispèsyon pigman |
Pi gran pase oswa egal a Klas 3 |
- |
||
|
Klas aparans: A1, A2, A3 oswa B |
||||
|
Revèsyon Longitudinal |
-PP cristalline-H |
Mwens pase oswa egal a 2% |
enMwens pase oswa egal a 8mm:1h 8mm＜enMwens pase oswa egal a 16mm:2h en> 16mm:4h |
(150±2) degre |
|
PP-B |
||||
|
PP-R |
(135±2) degre |
|||
|
-PP cristalline-RCT |
||||
|
Senpleman sipòte enpak gwo bout bwa |
-PP cristalline-H |
Pousantaj echèk Mwens pase oswa egal a 10% echantiyon |
Tanperati tès la |
(23±2) degre |
|
PP-B |
||||
|
PP-R |
(0±2) degre |
|||
|
-PP cristalline-RCT |
||||
|
Mas fonn -pousantaj koule (MFR) |
Mwens pase oswa egal a 0.5g / 10min ak mwens pase oswa egal a 20% varyasyon soti nan konpoze PP |
Tanperati tès Chajman pwa |
230 degre 2.16kg |
|
|
Estabilite tèmik anba presyon idrostatik |
Pa gen rupture, pa gen okenn flit |
Estrès idrostatik: -cristalline PP-H, PP-B, PP-R, -cristaline PP-RCT Tanperati tès Tanperati tès la |
1.9MPa 1.4MPa 1.9MPa 2.6MPa 110 degre 8760h |
|
|
Transmisyon limyè |
Mwens pase oswa egal a 0.2% |
- |
||
|
Transmisyon oksijèn |
Mwens pase oswa egal a 0.1g/(m3.d) |
|||
Karakteristik
Tiyo PP-R pa sèlman genyen avantaj jeneral nan tiyo plastik, tankou lejè, gwo fòs, rezistans korozyon, echèl-pwopriyete gratis, ak lavi sèvis long, men tou prezante karakteristik prensipal sa yo:
1.Eco -materyèl pou konstriksyon zanmitay: PP-R matyè premyè fè pati fanmi an polyolefin, ak molekil ki konpoze de eleman kabòn ak idwojèn, asire pèfòmans ijyenik serye.
2. Chalè-rezistan ak izolasyon, fè li yon pwodwi ekonomize enèji-.
3. Enstalasyon fasil ak serye: Koneksyon omojèn cho -fonn yo ka ranpli nan kèk segonn, pandan y ap bon jan kalite -metal-fitting entegre yo itilize pou koneksyon ak tiyo metal ak aparèy dlo, asire sekirite ak fyab.
Aplikasyon
1.Sistèm tiyo dlo frèt ak cho nan bilding, ki gen ladan sistèm chofaj santral.
2. Sistèm chofaj nan bilding yo, tankou anba planche, chofaj panèl miray, ak sistèm chofaj radyan.
3. Dirèk-sistèm rezèv dlo pwòp pou bwè.
4. Santral (santralize) è-sistèm kondisyone.
Baj popilè: ppr tiyo dlo, Lachin ppr tiyo dlo manifaktirè, Swèd, faktori